Soda-lime glass

Reusable soda-lime glass milk bottles
Old window made from soda-lime flat glass, Jena, Germany: The distorted reflections of a tree indicates that the flat glass was possibly not made by the float glass process.

Soda-lime glass, also called soda-lime-silica glass, is the most prevalent type of glass, used for windowpanes and glass containers (bottles and jars) for beverages, food, and some commodity items. Glass bakeware is often made of tempered soda-lime glass.[1] Soda-lime glass accounts for about 90% of manufactured glass.

Soda-lime glass is relatively inexpensive, chemically stable, reasonably hard, and extremely workable. Because it can be resoftened and remelted numerous times, it is ideal for glass recycling.[2]

Soda-lime glass is prepared by melting the raw materials, such as sodium carbonate (soda), lime, dolomite, silicon dioxide (silica), aluminium oxide (alumina), and small quantities of fining agents (e.g., sodium sulfate, sodium chloride) in a glass furnace at temperatures locally up to 1675 °C.[3] The temperature is only limited by the quality of the furnace superstructure material and by the glass composition. Relatively inexpensive minerals such as trona, sand, and feldspar are usually used instead of pure chemicals. Green and brown bottles are obtained from raw materials containing iron oxide. The mix of raw materials is termed batch.

Soda-lime glass is divided technically into glass used for windows, called flat glass, and glass for containers, called container glass. The two types differ in the application, production method (float process for windows, blowing and pressing for containers), and chemical composition. Flat glass has a higher magnesium oxide and sodium oxide content than container glass, and a lower silica, calcium oxide, and aluminium oxide content.[4] From the lower content of highly water-soluble ions (sodium and magnesium) in container glass comes its slightly higher chemical durability against water, which is required especially for storage of beverages and food.

Typical compositions and properties

Typical transmission spectrum of a 2-mm glass.[5]

The following table lists some physical properties of soda-lime glasses. Unless otherwise stated, the glass compositions and many experimentally determined properties are taken from one large study.[4] Those values marked in italic font have been interpolated from similar glass compositions (see calculation of glass properties) due to the lack of experimental data.

Properties Container glass Flat glass
Chemical
composition,
wt%
74 SiO2 0.3 K2O
13 Na2O 0.2 MgO
10.5 CaO 0.04 Fe2O3
1.3 Al2O3 0.01 TiO2
0.2 SO3
73 SiO2 0.03 K2O
14 Na2O 4 MgO
9 CaO 0.1 Fe2O3
0.15 Al2O3 0.02 TiO2
 
Viscosity
log(η, dPa·s or Poise)
= A + B / (T in °C − To)
550 °C (1,022 °F) 1,450 °C (2,640 °F)
A −2.309
B 3922
To 291
550 °C (1,022 °F) 1,450 °C (2,640 °F)
A −2.585
B 4215
To 263
Glass transition
temperature, Tg
573 °C (1,063 °F) 564 °C (1,047 °F)
Coefficient of
thermal expansion,
ppm/K, ~100–300 °C (212–572 °F)
9 9.5
Density
at 20 °C (68 °F), g/cm3
2.52 2.53
Refractive index
nD at 20 °C (68 °F)
1.518 1.520
Dispersion at 20 °C (68 °F),
104×(nF−nC)
86.7 87.7
Young's modulus
at 20 °C (68 °F), GPa
72 74
Shear modulus
at 20 °C (68 °F), GPa
29.8 29.8
Liquidus
temperature
1,040 °C (1,900 °F) 1,000 °C (1,830 °F)
Heat
capacity at 20 °C (68 °F),
J/(mol·K)
49 48
Surface tension,
at ~1,300 °C (2,370 °F), mJ/m2
315
Chemical durability,
Hydrolytic class,
after ISO 719[6]
3 3...4
Critical stress
intensity factor,[7]
(KIC), MPa.m0.5
? 0.75

See also

References

  1. "Pyrex Manufacturing History". World Kitchen Inc. Retrieved 2009-06-09.
  2. "Calcium Carbonate - Glass Manufacturing". congcal.com. congcal. Retrieved 5 August 2013.
  3. B. H. W. S. de Jong, "Glass"; in "Ullmann's Encyclopedia of Industrial Chemistry"; 5th edition, vol. A12, VCH Publishers, Weinheim, Germany, 1989, ISBN 3-527-20112-2, p 365-432.
  4. 1 2 "High temperature glass melt property database for process modeling"; Eds.: Thomas P. Seward III and Terese Vascott; The American Ceramic Society, Westerville, Ohio, 2005, ISBN 1-57498-225-7
  5. "Sodalime Optical Glass – Internal transmittance (2 mm)". vpglass.com. Archived from the original on 2011-09-09. Retrieved 2013-08-24.
  6. "ISO 719:1985 - Glass -- Hydrolytic resistance of glass grains at 98 degrees C -- Method of test and classification". iso.org.
  7. Wiederhorn, S.M. (1969). "Fracture stress energy of glass". Journal of the American Ceramic Society. 52 (2): 99–105. doi:10.1111/j.1151-2916.1969.tb13350.x.
  8. Gondret, P.; M. Lance; L. Petit (2002). "Bouncing Motion of Spherical Particles in Fluids". Physics of Fluids. 14 (2): 643–652. doi:10.1063/1.1427920.
  9. Janssen, L.P.B.M., Warmoeskerken, M.M.C.G., 2006. Transport phenomena data companion. Delft: VVSD.
  10. "Soda-Lime (Float) Glass Material Properties :: MakeItFrom.com". makeitfrom.com.
This article is issued from Wikipedia - version of the 11/26/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.