Lithium–air battery

Lithium–air battery
Specific energy 11,140 (theoretical) W·h/kg
Energy density ???
Specific power ???
Nominal cell voltage 2.91 V

The lithium-air battery, Li-air for short, is a metal-air battery chemistry that uses oxidation of lithium at the anode and reduction of oxygen at the cathode to induce a current flow.[1]

Originally proposed in the 1970s as a possible power source for battery electric vehicles, and hybrid electric vehicles. Li-air batteries recaptured scientific interest in the late 2000s due to advances in materials technology and an increasing demand for renewable energy sources.

Pairing lithium and oxygen (from air) can theoretically lead to electrochemical cells with the highest specific energy possible. Indeed, the theoretical specific energy of a non-aqueous Li-air battery (in the charged state with Li2O2 product and excluding the oxygen mass) is ~12 kWh/kg. This is comparable with the theoretical specific energy of gasoline (~13 kWh/kg). In practice, the Li-air batteries with a specific energy of ~1.7 kWh/kg at the cell level have been developed, which is about 5 times greater than that of commercial lithium-ion batteries, and which is sufficient to run a Fully Electric Vehicle (FEV) for 500 km (311 miles) on a single charge. (A 700 Wh/kg battery with an electric engine would be comparable with the internal combustion engine system in terms of the driving range per kg, while lithium ion batteries have only 105 Wh/kg at the pack level, i.e. they are limited to <150 km (93 miles) driving range). However, the areal power and cycle life of lithium –oxygen/air batteries need significant improvements before they can find any competitive market niche.

Significant advances in multiple fields are necessary to develop a commercial implementation.[2] Four approaches are active: aprotic,[3][4][5] aqueous,[6] solid state[7] and mixed aqueous/aprotic.[8]

Metal-air batteries, specifically zinc-air, have received attention due to potentially high energy densities. The theoretical specific energy densities for metal-air batteries are higher than for ion-based approaches. Lithium-air batteries can theoretically achieve 3840 mA·h/g.[9]

A major driver is the automotive sector. The energy density of gasoline is approximately 13 kW·h/kg, which corresponds to 1.7 kW·h/kg of energy provided to the wheels after losses. Theoretically lithium-air can achieve 12 kW·h/kg (43.2 MJ/kg) excluding the oxygen mass. Accounting for the weight of the full battery pack (casing, air channels, lithium substrate), however (lithium alone is very light), the energy density is expected to be considerably lower. Despite this, it would not be unreasonable to expect to be able deliver the same 1.7 kW·h/kg to the wheels as gasoline after the technology is fully developed, given the much higher efficiency of electric motors.[10]

Lithium-air batteries have the potential of 5–15 times the specific energy of current lithium-ion batteries.[11]

History

Although, the idea of lithium-air battery was around long before 1996,[12][13][14][15] the risks-to-benefits ratio for such technology was not perceived at that time as making it worth pursuing. Indeed, both the negative (lithium metal) and the positive (air or oxygen electrodes) are the reasons why, respectively, rechargeable lithium-metal batteries failed to get on the market in the 1970 (lithium-ion battery in your cell phone uses a LiC6-graphite compound on the negative electrode, not a lithium metal), and fuel cells failed during Hydrogen Economy epoch (2001-2009 in the USA). Nevertheless, due to the a perceived lack of other alternatives to high specific energy rechargeable batteries, and due to some initially promising results from academic labs (Abraham and Jiang 1996, Lu and Amine 2013), both the number of patents and of free-domain publications related to lithium-oxygen (including Li-air) batteries has been growing exponentially since ca. 2006 (Ogasawara, Débart et al. 2006, Lu and Amine 2013) (see Fig. 1). (The drop in the apparent patent number in the last 2 years is due to a delay between the priority and publication dates. For example, there is a 30-month delay between a Provisional Patent application being filed and a Patent Cooperation Treaty application being published.) However, the technical difficulties facing such batteries, especially considering that they have to be electrically rechargeable for most applications, are daunting (Lee, Roev et al. 2015).

Operation

Schematic of lithium-air battery charge and discharge cycles

Although details vary by battery design, in general, lithium ions move between the anode and the cathode sides across the electrolyte. Under discharge, electrons follow the external circuit to do electric work and the lithium ions migrate across the electrolyte. During charge (when an external potential becomes greater than the standard potential for the discharge reaction), the lithium metal plates onto the anode, freeing O
2 at the cathode.[16] Both non-aqueous(McCloskey, Burke et al. 2015) (with Li2O2 or LiO2 as the discharge products) and aqueous (LiOH as the discharge product) Li-O2 batteries have been considered.(Balaish, Kraytsberg et al. 2014, Imanishi and Yamamoto 2014) The aqueous battery requires a protective layer on the negative electrode to keep the Li metal from reacting with water.

Schematic of artificial vs. spontaneous electrolyte interface

Anode

Lithium metal is the typical anode choice. At the anode, electrochemical potential forces the lithium metal to give off electrons via oxidation (without involving the cathodic oxygen). The half reaction is:[17]

Li ↔ Li+ + e−

Lithium has high specific capacity (3840 mAh/g) compared with other metal-air battery materials (820 mAh/g for Zinc, 2965 mAh/g for aluminium).[18] Several issues affect such cells.

Upon charging/discharging in aprotic cells, layers of lithium salts precipitate onto the anode, eventually covering it and creating a barrier between the lithium and electrolyte. This barrier initially prevents corrosion, but eventually inhibits the reaction kinetics between the anode and the electrolyte.[19] This chemical change of the solid-electrolyte interface (SEI) results in varying chemical composition across the surface, causing the current to vary from point to point. The uneven current distribution furthers branching dendrite growth and typically leads to a short circuit between the anode and cathode.[20]

In aqueous cells problems at the SEI stem from the high reactivity of lithium metal with water.[21]

Several approaches have been taken to overcome problems at the SEI:

Cathode and electrolyte

At the cathode during charge, oxygen donates electrons to the lithium via reduction. Mesoporous carbon has been used as a cathode substrate with metal catalysts[25] that enhance reduction kinetics and increase the cathode's specific capacity.[11] Manganese, cobalt, ruthenium, platinum, silver, or a mixture of cobalt and manganese are under consideration as metal catalysts. Under some circumstances manganese-catalyzed cathodes performed best, with a specific capacity of 3137 mA·H/g carbon and cobalt-catalyzed cathodes performed second best, with a specific capacity of 2414 mA·H/g carbon.[26] Based on the first pore-scale modeling of lithium-air batteries, the microstructure of the cathode significantly affects battery capacity in both non-pore-blocking and pore-blocking regimes.[27]

Li-air cell performance is limited by the efficiency of reaction at the cathode because most of the voltage drop occurs there.[18] Multiple battery chemistries have been assessed, distinguished by electrolyte. This discussion focuses on aprotic and aqueous electrolytes as the solid-state electrochemistry is not well understood.

In a cell with an aprotic electrolyte lithium oxides are produced through reduction at the cathode:

Li+ + e− +O
2 + * → LiO
2*
Li+ + e− +LiO
2* →Li
2O
2*

where "*" denotes a surface site on Li
2O
2 where growth proceeds, which is essentially a neutral Li vacancy in the Li
2O
2 surface.

Lithium oxides are insoluble in aprotic electrolytes, which leads to cathode clogging.[28]

In a cell with an aqueous electrolyte the reduction at the cathode can also produce lithium hydroxide:

Acidic electrolyte

2Li + ½ O
2 + 2H+ → 2Li++ H
2O

A conjugate base is involved in the reaction. The theoretical maximal Li-air cell specific energy and Li-air cell energy density is 1400 W·h/kg and 1680 W·h/l, respectively.[10]

Alkaline aqueous electrolyte

2Li + ½ O
2 + H
2O → 2LiOH

Water molecules are involved in the redox reactions at the air cathode. The theoretical maximal Li-air cell specific energy and Li-air cell energy density is 1300 W·h/kg and 1520 W·h/l, respectively.[10]

The development of new cathode materials must account for the accommodation of substantial amounts of LiO
2, Li
2O
2 and/or LiOH without causing the cathode pores to block and employ suitable catalysts to make the electrochemical reactions energetically practical.

  • The first pore system serves as an oxidation product store.
  • The second pore system serves as oxygen transport.

Design

Cathode

A MnO
2 nanowire array cathode augmented by a genetically modified M13 virus offers two to three times the energy density of 2015 lithium-ion batteries. The virus increased the size of the nanowire array, which is about 80 nm across. The resulting wires had a spiked surface. Spikes create more surface area to host reaction sites. The viral process creates a cross-linked 3D structure, rather than isolated wires, stabilizing the electrode. The viral process is water-based and takes place at room temperature.[30][31]

Electrolyte

Efforts in Li-air batteries have focused on four different chemical designs. All the designs have distinct advantages and significant technical challenges.

Aprotic

Schematic of aprotic type Li-Air battery design

The non-aqueous Li-air batteries were demonstrated first (Abraham and Jiang 1996). They usually use the same mixed ethylene carbonate+ propylene carbonate solvents with LiPF6 or Li bis-sulfonimide salts like the conventional lithium-ion batteries, however, with a gelled rather than liquid electrolyte. (Imanishi, Matsui et al. 2014) The voltage difference upon constant current charge and discharge is usually between 1.3 and 1.8 V (with an OCP of ca. 4.2 V) even at such ridiculously low currents as 0.01-0.5 mA/cm² and 50-500 mA/g of C on the positive electrode (see Fig. 2 as an example).(Balaish, Kraytsberg et al. 2014, McCloskey, Burke et al. 2015, Liu, Xu et al. 2016) However, the carbonate solvents do evaporate and get oxidized due to a high overvoltage upon charge,(Lu and Amine 2013) and other solvents, such as end-capped glymes, DMSO, dimethylacetamide, and ionic liquids, have been considered.(Balaish, Kraytsberg et al. 2014, Imanishi, Matsui et al. 2014) Carbon cathode also gets oxidized above +3.5 V v Li during charge forming Li2CO3, which leads to an irreversible capacity loss.(Imanishi, Matsui et al. 2014)

Most effort involved aprotic materials, which consist of a lithium metal anode, a liquid organic electrolyte and a porous carbon cathode.[3] The electrolyte can be made of any organic liquid capable of solvating lithium salts such as LiPF
6, LiAsF
6, LiN(SO
2CF
3)
2, and LiSO
3CF
3), but typically consisted of carbonates, ethers and esters.[3][16] The carbon cathode is usually made of a high-surface-area carbon material with a nanostructured metal oxide catalyst (commonly MnO
2 or Mn
3O
4). A major advantage is the spontaneous formation of a barrier between anode and electrolyte (analogous to the barrier formed between electrolyte and carbon-lithium anodes in conventional Li-ion batteries) that protects the lithium metal from further reaction with the electrolyte. Although rechargeable,[10] the Li
2O
2 produced at the cathode is generally insoluble in the organic electrolyte, leading to buildup along the cathode/electrolyte interface. This makes cathodes in aprotic batteries prone to clogging and volume expansion that progressively reduces conductivity and degrades battery performance.[6][21][32] Another issue is that organic electrolytes are flammable and can ignite if the cell is damaged.[7]

In 2012, researchers announced that a dimethyl sulfoxide electrolyte and gold nanoparticle cathode achieved 100 charge cycles with 5% capacity loss.[33]

Although most studies agree that Li
2O
2 is the final discharge product of non-aqueous Li-O2 batteries, there is a considerable body of evidence that its formation does not proceed as a direct 2-electron electroreduction to peroxide O2−
2 (which is the common pathway for O2 reduction in water on carbon) but rather via a one–electron reduction to superoxide O−
2, followed by its disproportionation:

2LiO
2 = Li
2O
2+O
2 (1).

Superoxide (O−
2) has been traditionally considered as a dangerous intermediate in aprotic oxygen batteries due to its high nucleophilicity, basicity and redox potential.(Balaish, Kraytsberg et al. 2014, McCloskey, Burke et al. 2015) However, recent reports from Argonne (Zhai, Lau et al. 2015, Lu, Lee et al. 2016) suggest that superoxide (LiO2) is not just an intermediate during the discharge to peroxide (Li
2O
2) and but that that LiO2 can actually be used as the final discharge product, potentially with an improved cycle life albeit with a lower specific energy (a little heavier battery weight). Indeed, it was shown that under certain conditions the superoxide can be stable on the scale of 20-70 h at room temperature.(Zhai, Lau et al. 2015) Although an irreversible capacity loss upon disproportionation of LiO2 in the charged battery was not addressed in that work.

Pt/C seems to be the best electrocatalyst for O2 evolution and Au/C for O2 reduction when Li
2O
2 is the product.(Lu, Xu et al. 2010) Nevertheless, “the performance of rechargeable lithium-air batteries with non-aqueous electrolytes is limited by the reactions on the oxygen electrode, especially by O2 evolution… Conventional porous carbon air electrodes are unable to provide mAh/g and mAh/cm2 capacities and discharge rates at the magnitudes required for really high energy density batteries for EV applications.” (Lu, Xu et al. 2010) The capacity (in mAh/cm2) and the cycle life of the non-aqueous Li-O2 batteries is limited by the deposition of insoluble and poorly electronically conducting LiOx phases upon discharge.(Balaish, Kraytsberg et al. 2014) (It is worth noting that Li
3O
4 is predicted to have a better Li+ conductivity than the LiO2 and Li
2O
2 phases).(Shi, Xu et al. 2015) This makes the practical specific energy of Li-O2 batteries significantly smaller than the reagent-level calculation predicts. It seems that these parameters have reached their limitations by now, and further improvement can be expected only from alternative approaches.

Schematic of aqueous type Li-Air battery design

Aqueous

An aqueous Li-air battery consists of a lithium metal anode, an aqueous electrolyte and a porous carbon cathode. The aqueous electrolyte combines lithium salts dissolved in water. It avoids the issue of cathode clogging because the reaction products are water-soluble.[6] The aqueous design has a higher practical discharge potential than its aprotic counterpart. However, lithium metal reacts violently with water and thus the aqueous design requires a solid electrolyte interface between the lithium and electrolyte. Commonly, a lithium-conducting ceramic or glass is used, but conductivities are generally low (on the order of 10−3 S/cm at ambient temperatures).[21]

Schematic of a mixed aqueous-aprotic type Li-Air battery design

Mixed aqueous/aprotic

The aqueous/aprotic or mixed Li-air battery design attempts to unite advantages of the aprotic and aqueous battery designs. The common feature of hybrid designs is a two-part (one part aqueous and one part aprotic) electrolyte connected by a lithium-conducting membrane. The anode abuts the aprotic side while the cathode is in contact with the aqueous side. A lithium-conducting ceramic is typically employed as the membrane joining the two electrolytes.[6][10]

The use of a solid electrolyte (see Fig. 3) is one such alternative approaches that allows for a combination of a lithium metal anode with an aqueous cathode.(Visco 2004) Ceramic solid electrolytes (CSEs) of the NASICON type (e.g. Li1-xAxM2-x(PO4)3 with A ∈ [Al, Sc, Y] and M ∈ [Ti, Ge]) is one family of Li+ conducting materials that has been studied. Albeit compatible with water at alkaline pH and having a large electrochemical window (see Figs. 3,4), their low Li+ ion conductivity near room temperature (< 0.005 S/cm, >85 Ω cm2) (Imanishi, Matsui et al. 2014) makes them unsuitable for automotive and stationary energy storage applications which demand a low cost of power (i.e. operating current densities over 100 mA/cm2). Furthermore, both Ti and Ge are reduced by metallic Li, and an intermediate layer between the ceramic electrode and the negative electrode is required. On the other hand, solid polymer electrolytes (SPEs) can provide a higher conductivity but at the expense of a faster crossover of water and of other small molecules which are reactive toward metallic Li. Among the more exotic membranes considered for Li-O2 batteries is single-crystal silicon (Lu and Amine 2013).

In 2015 researchers announced a design that a used highly porous form of graphene for the anode, an electrolyte of lithium bis(trifluoromethyl) sulfonylimide/dimethoxyethane with added water and lithium iodide for use as a "mediator". The electrolyte produces lithium hydroxide (LiOH) at the cathode instead of lithium peroxide (Li
2O
2). The result offered energy efficiency of 93 percent (voltage gap of .2) and cycled more than 2,000 times with little impact on output.[34][35] However, the design required pure oxygen to function, rather than ambient air.[36]

Schematic of solid-state type Li-Air battery design

Solid state

The solid-state battery design is attractive from a safety standpoint, eliminating the possibility of ignition from rupture.[7] Current solid-state Li-air batteries use a lithium anode, a ceramic, glass, or glass-ceramic electrolyte, and a porous carbon cathode. The anode and cathode are typically separated from the electrolyte by polymer-ceramic composites that enhance charge transfer at the anode and electrochemically couple the cathode to the electrolyte. The polymer-ceramic composites reduce overall impedance. The main drawback of the solid-state battery design is the low conductivity of most glass-ceramic electrolytes. The ionic conductivity of current lithium fast ion conductors is still lower than liquid electrolyte alternatives.[9]

Challenges

As of 2013 many challenges confronted designers of Li-air batteries.

Cathode

Most of the current limitations in Li-air battery development are at the cathode, which is also the source of its potential advantages. Incomplete discharge due to blockage of the porous carbon cathode with discharge product such as lithium peroxide (in aprotic designs) is the most serious.

The effect of pore size and pore size distribution remains poorly understood.[18]

Catalysts have shown promise in creating preferential nucleation of Li
2O
2 over Li
2O, which is irreversible with respect to lithium.[37]

Atmospheric oxygen must be present at the cathode, but contaminants such as water vapor can damage it.[4]

Anode

The main challenge in anode development is preventing the anode from reacting with the electrolyte. Alternatives include new electrolyte materials or redesigning the interface between electrolyte and anode. Other challenges pertain to the particular choice of anode material, such as silicon or lithium. A great concern for silicon anodes is the large volume expansion (320%) it experiences as it alloys with lithium.[38] For lithium anodes, dendritic lithium deposits can form, decreasing energy capacity or triggering a short circuit.[39]

Electrochemical

In current cell designs, the charge overpotential is much higher than the discharge overpotential. Significant charge overpotential indicates the presence of secondary reactions.[40] As a result, electrical efficiency is only around 65%.[18]

Catalysts such as MnO
2, Co, Pt and Au can potentially reduce the overpotentials, but the effect is poorly understood.[37] Several catalysts improve cathode performance, notably MnO
2. The mechanism of improvement is unknown, but may alter the structure of the oxide deposits.[41][42]

Significant drops in cell capacity with increasing discharge rates are another issue. The decrease in cell capacity is attributed to kinetic charge transfer limitations.[18] Since the anodic reaction occurs very quickly, the charge transfer limitations are thought to occur at the cathode.

Stability

Long term battery operation requires chemical stability of all cell components. Current cell designs show poor resistance to oxidation by reaction products and intermediates. Many aqueous electrolytes are volatile and can evaporate over time.[18] Stability is hampered in general by parasitic chemical reactions taking place for instance those involving reactive oxygen.,[43][44]

Applications

Vehicles

Li-air cells are of interest for electric vehicles because they have a high theoretical specific and volumetric energy density (when balance of plant is ignored), comparable to petrol Electric motors provide high efficiency (95% compared to 35% for an internal combustion engine. Li-air cells could offer range equivalent to today's vehicles with a battery pack ⅓ the size of standard fuel tanks assuming the balance of plant required to maintain the battery was of negligible mass or volume.

Grid backup

In 2014, researchers announced a hybrid solar cell/battery. Up to 20% of the energy produced by conventional solar cells is lost as it travels to and charges a battery. The hybrid stores nearly 100% of the energy produced. The first version of the hybrid used a potassium-air battery. It offered higher energy density than conventional Li-ion batteries, was less expensive and avoided toxic byproducts. The latest device essentially substituted lithium for potassium.[45]

The solar cell used a mesh made from microscopic rods of titanium dioxide to allow the required oxygen to pass through. Captured sunlight produced electrons that decompose lithium peroxide into lithium ions, thereby charging the battery. During discharge, oxygen from air replenished the lithium peroxide.[45]

See also

References

  1. ↑ Badwal, Sukhvinder P. S.; Giddey, Sarbjit S.; Munnings, Christopher; Bhatt, Anand I.; Hollenkamp, Anthony F. (24 September 2014). "Emerging electrochemical energy conversion and storage technologies". Frontiers in Chemistry. 2. doi:10.3389/fchem.2014.00079.
  2. ↑ Christensen, J.; Albertus, P.; Sanchez-Carrera, R. S.; Lohmann, T.; Kozinsky, B.; Liedtke, R.; Ahmed, J.; Kojic, A. (2012). "A Critical Review of Li∕Air Batteries". Journal of the Electrochemical Society. 159 (2): R1. doi:10.1149/2.086202jes.
  3. 1 2 3 Younesi, Reza; Veith, Gabriel M.; Johansson, Patrik; Edström, Kristina; Vegge, Tejs (2015). "Lithium salts for advanced lithium batteries: Li–metal, Li–O 2 , and Li–S". Energy Environ. Sci. 8 (7): 1905–1922. doi:10.1039/c5ee01215e.
  4. 1 2 Ogasawara, T.; Débart, A. L.; Holzapfel, M.; Novák, P.; Bruce, P. G. (2006). "Rechargeable Li2O2Electrode for Lithium Batteries". Journal of the American Chemical Society. 128 (4): 1390–1393. doi:10.1021/ja056811q. PMID 16433559.
  5. ↑ Debart A, Bao,J et al (2008). "α-MnO
    2     Nanowires: A Catalyst for theO
    2     Electrode in Rechargeable Lithium Batteries",Angew.Chem.,47(24):p.4521-4524.
  6. 1 2 3 4 He, P.; Wang, Y.; Zhou, H. (2010). "A Li-air fuel cell with recycle aqueous electrolyte for improved stability". Electrochemistry Communications. 12 (12): 1686. doi:10.1016/j.elecom.2010.09.025.
  7. 1 2 3 4 Kumar, B.; Kumar, J.; Leese, R.; Fellner, J. P.; Rodrigues, S. J.; Abraham, K. M. (2010). "A Solid-State, Rechargeable, Long Cycle Life Lithium–Air Battery". Journal of the Electrochemical Society. 157: A50. doi:10.1149/1.3256129.
  8. ↑ Wang, Yonggang (2010). "A lithium-air battery with a potential to continuously reduce O2 from air for delivering energy". Journal of Power Sources. 195 (1): 358–361. doi:10.1016/j.jpowsour.2009.06.109.
  9. 1 2 Kumar, B.; Kumar, J. (2010). "Cathodes for Solid-State Lithium–Oxygen Cells: Roles of Nasicon Glass-Ceramics". Journal of the Electrochemical Society. 157 (5): A611. doi:10.1149/1.3356988.
  10. 1 2 3 4 5 Girishkumar, G.; McCloskey, B.; Luntz, A. C.; Swanson, S.; Wilcke, W. (2010). "Lithium−Air Battery: Promise and Challenges". The Journal of Physical Chemistry Letters. 1 (14): 2193. doi:10.1021/jz1005384.
  11. 1 2 Ed. Jurgen O. Besenhard, Handbook of Battery Materials,New Your, Wiley-VCH, 1999, ISBN 3-527-29469-4.
  12. ↑ Abraham and Jiang 1996
  13. ↑ Lu and Amine 2013
  14. ↑ Balaish, Kraytsberg et al. 2014
  15. ↑ Lu, Li et al. 2014
  16. 1 2 Xu, K. (2004). "Nonaqueous Liquid Electrolytes for Lithium-Based Rechargeable Batteries". Chemical Reviews. 104 (10): 4303–417. doi:10.1021/cr030203g. PMID 15669157.
  17. ↑ Winter, M.; Brodd, R. J. (2004). "What Are Batteries, Fuel Cells, and Supercapacitors?". Chemical Reviews. 104 (10): 4245–4269. doi:10.1021/cr020730k. PMID 15669155.
  18. 1 2 3 4 5 6 Kraytsberg, A.; Ein-Eli, Y. (2011). "Review on Li–air batteries—Opportunities, limitations and perspective". Journal of Power Sources. 196 (3): 886. doi:10.1016/j.jpowsour.2010.09.031.
  19. ↑ Aurbach, D. (2000). "Review of selected electrode–solution interactions which determine the performance of Li and Li ion batteries". Journal of Power Sources. 89 (2): 206–218. doi:10.1016/S0378-7753(00)00431-6.
  20. ↑ Whittingham, M. S. (1976). "Electrical Energy Storage and Intercalation Chemistry". Science. 192 (4244): 1126–1127. doi:10.1126/science.192.4244.1126. PMID 17748676.
  21. 1 2 3 Kowalczk, I.; Read, J.; Salomon, M. (2007). "Li-air batteries: A classic example of limitations owing to solubilities". Pure and Applied Chemistry. 79 (5): 851. doi:10.1351/pac200779050851.
  22. 1 2 Singh, M.; Gur, I.; Balsara, N. P.(2009). "Solid Electrolyte Material Manufacturable by Polymer Processing Methods", U.S. Patent Application #12271829.
  23. ↑ Bates, J. (2000). "Thin-film lithium and lithium-ion batteries". Solid State Ionics. 135: 33–37. doi:10.1016/S0167-2738(00)00327-1.
  24. ↑ Visco, S.; Nimonm, Y. (2010). "Active Metal/Aqueous Electrochemical Cells and Systems", U.S.Patent #7645543.
  25. ↑ New Energy and Fuel. 2011. Accessed 20 Nov. 2011
  26. ↑ Abraham, K. M. (1996). "A Polymer Electrolyte-Based Rechargeable Lithium/Oxygen Battery". Journal of the Electrochemical Society. 143: 1–0. doi:10.1149/1.1836378.
  27. ↑ Charles P. Andersen, Han Hu, Gang Qiu, Vibha Kalra, and Ying Sun, "Pore-Scale Transport Resolved Model Incorporating Cathode Microstructure and Peroxide Growth in Lithium-Air Batteries", J. Electrochem. Soc., 162, (2015) A1135-A1145
  28. ↑ Read, J. (2002). "Characterization of the Lithium/Oxygen Organic Electrolyte Battery". Journal of the Electrochemical Society. 149 (9): A1190–A1196. doi:10.1149/1.1498256.
  29. ↑ Williford, R. E.; Zhang, J. G. (2009). "Air electrode design for sustained high power operation of Li/air batteries". Journal of Power Sources. 194 (2): 1164. doi:10.1016/j.jpowsour.2009.06.005.
  30. ↑ "Lithium-air batteries go viral for greater durability and performance". gizmag.com.
  31. ↑ Oh, D.; Qi, J.; Lu, Y. C.; Zhang, Y.; Shao-Horn, Y.; Belcher, A. M. (2013). "Biologically enhanced cathode design for improved capacity and cycle life for lithium-oxygen batteries". Nature Communications. 4. doi:10.1038/ncomms3756.
  32. ↑ Li, Xianglin; Faghri, Amir (2012). "Optimization of the Cathode Structure of Lithium-Air Batteries Based on a Two-Dimensional, Transient, Non-Isothermal Model". Journal of Electrochemical Society. 159 (10): A1747–A1754. doi:10.1149/2.043210jes.
  33. ↑ Service, Robert F. "An Electric Car That Actually Goes Far? – ScienceNOW". News.sciencemag.org. Retrieved 2012-07-20.
  34. ↑ Delacey, Lynda (November 19, 2015). "More hurdles jumped on path to a practical lithium-air battery". www.gizmag.com. Retrieved 2015-12-03.
  35. ↑ Liu, Tao; Leskes, Michal; Yu, Wanjing; Moore, Amy J.; Zhou, Lina; Bayley, Paul M.; Kim, Gunwoo; Grey, Clare P. (2015-10-30). "Cycling Li-O2 batteries via LiOH formation and decomposition". Science. 350 (6260): 530–533. doi:10.1126/science.aac7730. ISSN 0036-8075. PMID 26516278.
  36. ↑ "New design points a path to the 'ultimate' battery". phys.org. October 29, 2015. Retrieved 2015-12-03.
  37. 1 2 Lu, Yi-Chun (2010). "The Influence of Catalysts on Discharge and Charge Voltages of Rechargeable Li–Oxygen Batteries". Electrochemical and Solid-State Letters. 13 (6): A69. doi:10.1149/1.3363047.
  38. ↑ Mukhopadhyay, Amartya; Sheldon, Brian W. (2014-06-01). "Deformation and stress in electrode materials for Li-ion batteries". Progress in Materials Science. 63: 58–116. doi:10.1016/j.pmatsci.2014.02.001.
  39. ↑ Tikekar, Mukul D.; Choudhury, Snehashis; Tu, Zhengyuan; Archer, Lynden A. (2016-09-08). "Design principles for electrolytes and interfaces for stable lithium-metal batteries". Nature Energy. 1 (9). doi:10.1038/nenergy.2016.114. ISSN 2058-7546.
  40. ↑ Zhang, T.; Imanishi, N.; Shimonishi, Y.; Hirano, A.; Takeda, Y.; Yamamoto, O.; Sammes, N. (2010). "A novel high energy density rechargeable lithium/air battery". Chemical Communications. 46 (10): 1661–1663. doi:10.1039/b920012f. PMID 20177608.
  41. ↑ Darren Quick (5 April 2010). "Lithium-air batteries offer three times the energy density". Retrieved 5 Oct 2011.
  42. ↑ Shimonishi, Y.; Zhang, T.; Imanishi, N.; Im, D.; Lee, D. J.; Hirano, A.; Takeda, Y.; Yamamoto, O.; Sammes, N. (2011). "A study on lithium/air secondary batteries—Stability of the NASICON-type lithium ion conducting solid electrolyte in alkaline aqueous solutions". Journal of Power Sources. 196 (11): 5128. doi:10.1016/j.jpowsour.2011.02.023.
  43. ↑ Why Do Lithium–Oxygen Batteries Fail: Parasitic Chemical Reactions and Their Synergistic Effect X. Yao, Q. Dong, Q. Cheng, D. Wang, Angew. Chem. Int. Ed. 2016, 55, 11344. doi:10.1002/anie.201601783
  44. ↑ Singlet Oxygen Formation during the Charging Process of an Aprotic Lithium–Oxygen Battery J. Wandt, P. Jakes, J. Granwehr, H.A. Gasteiger, R.-A. Eichel, Angew. Chem. Int. Ed. 2016, 128, 7006–7009. {{doi: 10.1002/anie.201602142}}
  45. 1 2 DIMBERUON, PENIEL M. (October 28, 2014). "New Hybrid Solar Cell Battery Takes Aim at Solar Power's Energy Storage Problem". Singularity Hub. Retrieved February 2015. Check date values in: |access-date= (help)
This article is issued from Wikipedia - version of the 11/13/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.