Kraft process

International Paper: Kraft paper mill

The kraft process (also known as kraft pulping or sulfate process)[1] is a process for conversion of wood into wood pulp, which consists of almost pure cellulose fibers, the main component of paper. The kraft process entails treatment of wood chips with a hot mixture of water, sodium hydroxide, and sodium sulfide, known as white liquor, that breaks the bonds that link lignin, hemicellulose, and cellulose. The technology entails several steps, both mechanical and chemical. It is the dominant method for producing paper. In some situations, the process has been controversial because kraft plants can release smelly products and in some situations produce substantial liquid wastes.[2]


The kraft process (so called because of the superior strength of the resulting paper, from the German word Kraft for 'strength') was invented by Carl F. Dahl in 1879 in Danzig, Prussia, Germany. U.S. Patent 296,935 was issued in 1884, and a pulp mill using this technology started (in Sweden) in 1890.[3] The invention of the recovery boiler by G.H. Tomlinson in the early 1930s was a milestone in the advancement of the kraft process.[4] It enabled the recovery and reuse of the inorganic pulping chemicals such that a kraft mill is a nearly closed-cycle process with respect to inorganic chemicals, apart from those used in the bleaching process. For this reason, in the 1940s, the kraft process superseded the sulfite process as the dominant method for producing wood pulp.[3]

The process

Continuous kraft pulp mill


Common wood chips used in pulp production are 12–25 millimetres (0.47–0.98 in) long and 2–10 millimetres (0.079–0.394 in) thick. The chips normally first enter the presteaming where they are wetted and preheated with steam. Cavities inside fresh wood chips are partly filled with liquid and partly with air. The steam treatment causes the air to expand and about 25% of the air to be expelled from the chips. The next step is to saturate the chips with black and white liquor. Air remaining in chips at the beginning of liquor impregnation is trapped within the chips. The impregnation can be done before or after the chips enters the digester and is normally done below 100 °C (212 °F). The cooking liquors consist of a mixture of white liquor, water in chips, condensed steam and weak black liquor. In the impregnation, cooking liquor penetrates into the capillary structure of the chips and low temperature chemical reactions with the wood begin. A good impregnation is important to get a homogeneous cook and low rejects. About 40–60% of all alkali consumption in the continuous process occurs in the impregnation zone.


The wood chips are then cooked in pressurized vessels called digesters. Some digesters operate in a batch manner and some in a continuous process. There are several variations of the cooking processes both for the batch and the continuous digesters. Digesters producing 1,000 tonnes or more of pulp per day are common, with the largest producing more than 3,500 tonnes per day.[5] In a continuous digester, the materials are fed at a rate which allows the pulping reaction to be complete by the time the materials exit the reactor. Typically, delignification requires several hours at 170 to 176 °C (338 to 349 °F). Under these conditions lignin and hemicellulose degrade to give fragments that are soluble in the strongly basic liquid. The solid pulp (about 50% by weight of the dry wood chips) is collected and washed. At this point the pulp is known as brown stock because of its color. The combined liquids, known as black liquor (because of its color), contain lignin fragments, carbohydrates from the breakdown of hemicellulose, sodium carbonate, sodium sulfate and other inorganic salts.

net reaction in depolymerization of lignin by SH (Ar = aryl, R = alkyl groups).

One of the main chemical reactions that underpin the kraft process is the scission of ether bonds by the nucleophilic sulfide (S2−) or bisulfide (HS) ions.[4]

Recovery process

The excess black liquor contains about 15% solids and is concentrated in a multiple effect evaporator. After the first step the black liquor has about 20 - 30% solids. At this concentration the rosin soap rises to the surface and is skimmed off. The collected soap is further processed to tall oil. Removal of the soap improves the evaporation operation of the later effects.

The weak black liquor is further evaporated to 65% or even 80% solids ("heavy black liquor"[6]) and burned in the recovery boiler to recover the inorganic chemicals for reuse in the pulping process. Higher solids in the concentrated black liquor increases the energy and chemical efficiency of the recovery cycle, but also gives higher viscosity and precipitation of solids (plugging and fouling of equipment).[7][8] During combustion sodium sulfate is reduced to sodium sulfide by the organic carbon in the mixture:

1. Na2SO4 + 2 C → Na2S + 2 CO2

This reaction is similar to thermochemical sulfate reduction in geochemistry.

The molten salts ("smelt") from the recovery boiler are dissolved in a process water known as "weak wash." This process water, also known as "weak white liquor" is composed of all liquors used to wash lime mud and green liquor precipitates. The resulting solution of sodium carbonate and sodium sulfide is known as "green liquor", although it is not known exactly what causes the liquor to be green. This liquid is mixed with calcium oxide, which becomes calcium hydroxide in solution, to regenerate the white liquor used in the pulping process through an equilibrium reaction (Na2S is shown since it is part of the green liquor, but does not participate in the reaction):

2. Na2S + Na2CO3 + Ca(OH)2 ←→ Na2S + 2 NaOH + CaCO3

Calcium carbonate precipitates from the white liquor and is recovered and heated in a lime kiln where it is converted to calcium oxide (lime).

3. CaCO3 → CaO + CO2

Calcium oxide (lime) is reacted with water to regenerate the calcium hydroxide used in Reaction 2:

4. CaO + H2O → Ca(OH)2

The combination of reactions 1 through 4 form a closed cycle with respect to sodium, sulfur and calcium and is the main concept of the so-called recausticizing process where sodium carbonate is reacted to regenerate sodium hydroxide.

The recovery boiler also generates high pressure steam which is fed to turbogenerators, reducing the steam pressure for the mill use and generating electricity. A modern kraft pulp mill is more than self-sufficient in its electrical generation and normally will provide a net flow of energy which can be used by an associated paper mill or sold to neighboring industries or communities through to the local electrical grid.[9] Additionally, bark and wood residues are often burned in a separate power boiler to generate steam.

Although recovery boilers using G.H. Tomlinson's invention have been in general use since the early 1930s attempts have been made to find a more efficient process for the recovery of cooking chemicals. Weyerhaeuser has operated a Chemrec first generation black liquor entrained flow gasifier successfully at its New Bern plant in North Carolina, while a second generation plant is run in pilot scale at Smurfit Kappa's plant in Piteå, Sweden.[10]


The finished cooked wood chips are blown to a collection tank called a blow tank that operates at atmospheric pressure. This releases a lot of steam and volatiles. The volatiles are condensed and collected; in the case of northern softwoods this consists mainly of raw turpentine.


Screening of the pulp after pulping is a process whereby the pulp is separated from large shives, knots, dirt and other debris. The accept is the pulp. The material separated from the pulp is called reject.

The screening section consists of different types of sieves (screens) and centrifugal cleaning. The sieves are normally set up in a multistage cascade operation because considerable amounts of good fibres can go to the reject stream when trying to achieve maximum purity in the accept flow.

The fiber containing shives and knots are separated from the rest of the reject and reprocessed either in a refiner and/or is sent back to the digester. The content of knots is typically 0.5 - 3.0% of the digester output, while the shives content is about 0.1- 1.0%.


The brownstock from the blowing goes to the washing stages where the used cooking liquors are separated from the cellulose fibers. Normally a pulp mill has 3-5 washing stages in series. Washing stages are also placed after oxygen delignification and between the bleaching stages as well. Pulp washers use counter current flow between the stages such that the pulp moves in the opposite direction to the flow of washing waters. Several processes are involved: thickening / dilution, displacement and diffusion. The dilution factor is the measure of the amount of water used in washing compared with the theoretical amount required to displace the liquor from the thickened pulp. Lower dilution factor reduces energy consumption, while higher dilution factor normally gives cleaner pulp. Thorough washing of the pulp reduces the chemical oxygen demand (COD).

Several types of washing equipment are in use:


In a modern mill, brownstock (cellulose fibers containing approximately 5% residual lignin) produced by the pulping is first washed to remove some of the dissolved organic material and then further delignified by a variety of bleaching stages.[11]

In the case of a plant designed to produce pulp to make brown sack paper or linerboard for boxes and packaging, the pulp does not always need to be bleached to a high brightness. Bleaching decreases the mass of pulp produced by about 5%, decreases the strength of the fibers and adds to the cost of manufacture.

Process chemicals

Process chemicals are added to improve the production process:

Comparison with other pulping processes

Pulp produced by the kraft process is stronger than that made by other pulping processes and maintaining a high effective sulfur ratio or sulfidity is important for the highest possible strength. Acidic sulfite processes degrade cellulose more than the kraft process, which leads to weaker fibers. Kraft pulping removes most of the lignin present originally in the wood whereas mechanical pulping processes leave most of the lignin in the fibers. The hydrophobic nature of lignin[14] interferes with the formation of the hydrogen bonds between cellulose (and hemicellulose) in the fibers needed for the strength of paper[3] (strength refers to tensile strength and resistance to tearing).

Kraft pulp is darker than other wood pulps, but it can be bleached to make very white pulp. Fully bleached kraft pulp is used to make high quality paper where strength, whiteness and resistance to yellowing are important.

The kraft process can use a wider range of fiber sources than most other pulping processes. All types of wood, including very resinous types like southern pine,[15] and non-wood species like bamboo and kenaf can be used in the kraft process.

Byproducts and emissions

The main byproducts of kraft pulping are crude sulfate turpentine and tall oil soap. The availability of these is strongly dependent on wood species, growth conditions, storage time of logs and chips, and the mill's process.[16] Pines are the most extractive rich woods. The raw turpentine is volatile and is distilled of the digester, while the raw soap is separated from the spent black liquor by decantation of the soap layer formed on top of the liquor storage tanks. From pines the average yield of turpentine is 5–10 kg/t pulp and of crude tall oil is 30–50 kg/t pulp.[16]

Various byproducts containing hydrogen sulfide, methyl mercaptan, dimethyl sulfide, dimethyl disulfide, and other volatile sulfur compounds are the cause of the malodorous air emissions characteristic for pulp mills utilizing the kraft process. Outside the modern mills the odour is perceivable only during disturbance situations, for example when shutting the mill down for maintenance break. This is due to practiced collection and burning of these odorous gases in the recovery boiler along with black liquor. The sulfur dioxide emissions of the kraft pulp mills are much lower than sulfur dioxide emissions from sulfite mills. In modern mills where high dry solids are burned in the recovery boiler hardly any sulfur dioxide leaves the boiler. This is mainly due to higher lower furnace temperature which leads to higher sodium release from the black liquor droplets that can react with sulfur dioxide forming sodium sulfate.

Pulp mills are almost always located near large bodies of water due to their former substantial demands. Delignification of chemical pulps released considerable amounts of organic material into the environment, particularly into rivers or lakes. The wastewater effluent can also be a major source of pollution, containing lignins from the trees, high biological oxygen demand (BOD) and dissolved organic carbon (DOC), along with alcohols, chlorates, heavy metals, and chelating agents. Reducing the environmental impact of this effluent is accomplished by closing the loop and recycling the effluent where possible, as well as employing less damaging agents in the pulping and bleaching processes. The process effluents are treated in a biological effluent treatment plant, which guarantees that the effluents are not toxic in the recipient.

See also

Further reading


  1. The process name is derived from German Kraft, meaning "strength" in this context, due to the strength of the kraft paper produced using this process. Both capitalized and lowercase spelling ("Kraft process" and "kraft process") appear in the literature, but "kraft" is most commonly used in the pulp and paper industry.
  2. Rudolf Patt et al. "Paper and Pulp" in Ullmann's Encyclopedia of Industrial Chemistry 2002 Wiley-VCH, Weinheim. doi:10.1002/14356007.a18_545.pub4
  3. 1 2 3 Biermann, Christopher J. (1993). Essentials of Pulping and Papermaking. San Diego: Academic Press, Inc. ISBN 0-12-097360-X.
  4. 1 2 E. Sjöström (1993). Wood Chemistry: Fundamentals and Applications. Academic Press. ISBN 0-12-647480-X.
  5. Woodman, Jocelyn (1993). "Pollution Prevention Technologies for the Bleached Kraft Segment of the U.S. Pulp and Paper Industry (see p 66)" (PDF). U.S. Environmental Protection Agency. Retrieved 2007-09-11.
  6. "Equipment to handle heavy black liquor". Retrieved 2007-10-09.
  7. Hsieh, Jeffery S.; Smith, Jason B. "Second Critical Solids Black Liquor Scaling" (PDF). Pulp and Paper Engineering, School of Chemical Engineering, Georgia Institute of Technology. Retrieved 2007-10-09.
  8. US granted 5527427, Mualla Berksoy & Yaman Boluk, "High solids black liquor of reduced viscosity and viscosity reduction method for high solids black liquor", issued 1996-06-18, assigned to Optima Specialty Chemicals & Technology Inc
  9. Jeffries, Tom (March 27, 1997). "Kraft pulping: Energy consumption and production". University of Wisconsin Biotech Center . Retrieved 2007-10-21. External link in |publisher= (help)
  10. Chemrec web site
  11. "Environmental Comparison of Bleached Kraft Pulp ManufacturingTechnologies" (PDF). Retrieved 2007-09-28.
  12. Goyal, Gopal C. (1997). Anthraquinone Pulping. A TAPPI Press Anthology of Published Papers, 1977-1996. Atlanta: TAPPI Press. ISBN 0-89852-340-0.
  14. Hubbe, Martin a.; Lucian A. Lucia (2007). "The "Love-Hate" Relationship Present in Lignocellulosic Materials". BioResources. 2 (4): 534–535. Retrieved 2015-02-03.
  15. "The Southern Pines" (PDF). US Department of Agriculture. 1985. Retrieved 2007-09-13.
  16. 1 2 Stenius, Per, ed. (2000). "2". Forest Products Chemistry. Papermaking Science and Technology. 3. Helsinki, Finland: Fapet OY. pp. 73–76. ISBN 952-5216-03-9..
Wikimedia Commons has media related to Kraft process.
This article is issued from Wikipedia - version of the 11/4/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.