High frequency impact treatment

Example of a HiFIT treated assembly

High Frequency Impact Treatment or HiFIT - Method is the treatment of welded steel constructions at the weld transition to increase the fatigue strength.

Features

The durability and life of dynamically loaded, welded steel structures is determined in many cases by the welds, particular the weld transitions. Through selective treatment of the transitions (grinding (abrasive cutting) abrasive blasting, hammering, etc.), the durability of many designs increase significantly. Hammering methods have proven to be particularly effective treatment methods and were within the joint project REFRESH[1] extensively studied and developed. The HiFIT process (High Frequency Impact Treatment) is such a hammering method that is universally applicable, requires only a low tech equipment and still offers high reproducibility and the possibility for quality control.

Operation

HiFIT-hammer

The HiFIT hammer operates with a hardened pin with a ball resting on the workpiece with a diameter D of 3 mm.[2] This pin is hammered with an adjustable intensity at around 180–300 Hz at the weld toe. Local mechanical deformations occur in the form of a treatment track. The weld toe is deformed plastically and bonded. The induced compressive residual stresses in the treatment prevent the track cracking and the crack propagation on the surface.

Evidence

The International Institute of Welding Technology IIW published the Guideline "Recommendations for the HFMI Treatment" in October 2016. An overview of higher frequency hammers (HFMI) is presented, and recommendations for the correct application of the method and quantitative measurements for quality assurance the guideline provides the basis for measurements of HFMI improved welded joints on the basis of all known stress calculation concepts.

In numerous experiments at various institutes and universities an 80 to 100 percent increase of fatigue strength and a 5 - to 15-fold increase in weld-life could be demonstrated. The most extensive research project was from 2006-2009 "REFRESH - life extension of existing and new welded steel structures (P702). In this research project, the HiFIT device was developed and made ready for production. This report is available in book form at the FOSTA (Forschungsvereinigung Stahlanwendung e.V.) and can be ordered under the number ISBN 978-3-942541-03-9. The book contains detailed scientific verifications and validations.

Steps in the HiFIT method

The HiFIT method can be applied to both existing as well as new steel structures.

Preliminary steps

For a targeted treatment, the visibility and accessibility of the transition in the welded areas are required. Existing structures typically are prepared at the transition for surface finishing. The parts must be free of loose rust and old paint. If necessary, previous sandblasting is required.

The device operates with a compressed air supply of 6-8 bar.

Steps

HiFIT device is manually placed on the treated weld transition and during treatment, along this run.

Result

By local transformations, the weld toe plastically deformed and solidified. The depth of the aftertreatment track should be between 0.2 and 0.35 mm. The undercut at the weld toe is no longer recognizable.

Process Safety

By visual inspection, the treated region are examined. The treatment depth can be checked with a special gauge. A digital display of the operating pressure allows the user to control the whole time.

Economic importance of the HiFIT method

Lifetime extension

When applied to existing constructions, the lifetime can be extended considerably. If no macroscopically visible cracks are present, HiFIT is a very suitable remediation tool. With timely remediation of existing structures there is practically no difference to the life of new treated welds. This gives the potential to use existing constructions far beyond the planned lifetime. The HiFIT-method is used very efficient e.g. at highway bridges in steel hollow box-section design on the fly. Costs for reconstruction are low compared to conventional methods. In the commercial vehicle industry and other industries highly stressed welds on existing and new structures are treated with HiFIT to extend lifetime successfully.

Increasing the transferable load level

In case of new constructions and for some existing structures the load level for treated welds can be increased. Using constructions for the same lifetime as before welds can transfer 1.6 times loads. This has e.g. for cranes the very positive effect of larger lifting capacity. The efficiency of cranes increases with each stroke.

Lightweight

Taking into account the HiFIT process during development, on same load level and same lifetime, the construction can be slimmed down specifically. Extensive experimental investigations on structural details and FEM-supported-design methods has shown the high efficiency with conventional S235, S355J2 and fine grain steels, such as S460N, S690QL and even higher strength steels. The achievable material saving makes the HiFIT application in most applications already economically viable. Considering the additional benefit of the weight advantage e.g. the achievable payload in vehicles can be increased.

See also

Publications

References

  1. Website of the Karlsruhe Institute of Technology (KIT) - Project REFRESH
  2. Th Nitschke-Pagel, Klaus Dilger, H.Eslami, I.Weich, T.Ummenhofer. "Residual stresses and near surface material condition of welded high strength steels after different mechanical post-weld treatments" . 2008.

External links

This article is issued from Wikipedia - version of the 11/8/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.