Gold plating

For other uses, see Gold plating (disambiguation).
Gold-plated aluminium cover on Voyager space craft that protects a gold-plated Sounds of Earth record
A gold plated desktop Stirling engine

Gold plating is a method of depositing a thin layer of gold onto the surface of another metal, most often copper or silver (to make silver-gilt), by chemical or electrochemical plating. This article covers plating methods used in the modern electronics industry; for more traditional methods, often used for much larger objects, see gilding.

Gold plating types

There are several types of gold plating used in the electronics industry:[1]

In ancient America

Pre-Columbian smiths working in northern Peru gilded and silvered copper objects by electrochemical replacement techniques.[2]

During the excavations in 1987–1990 at Sipan, a spectacular treasure of gold and silver ornamental and ceremonial artifacts was recovered, dating to AD 50–300. These objects demonstrate the outstanding craftsmanship of the Moche metalsmiths. Alloys of copper with gold and some silver were employed, known as tumbaga.[3]

Gold plating chemistry

There are five recognized classes of gold plating chemistry:

  1. Alkaline gold cyanide, for gold and gold alloy plating
  2. Neutral gold cyanide, for high-purity plating
  3. Acid gold plating for bright hard gold and gold alloy plating
  4. Non-cyanide, generally sulphite or chloride-based for gold and gold alloy plating
  5. Miscellaneous

Jewelry

Gold plating of silver is used in the manufacture of jewelry. Like copper, silver atoms diffuse into the gold layer, causing slow gradual fading of its color and eventually causing tarnishing of the surface. This process may take months and even years, depending on the thickness of the gold layer. A barrier metal layer is used to counter this effect. Copper, which also migrates into gold, does so more slowly than silver. The copper is usually further plated with nickel. A gold-plated silver article is usually a silver substrate with layers of copper, nickel, and gold deposited on top of it.

Infrared Reflectivity

Gold, applied by either evaporated methods or Electroplating has been specified by NASA to thermally control spacecraft instruments thanks to its 99% reflectivity in Infrared Wavelengths.

Electronics

Gold-plated electrical connectors

Gold plating is often used in electronics, to provide a corrosion-resistant electrically conductive layer on copper, typically in electrical connectors and printed circuit boards.

With direct gold-on-copper plating, the copper atoms tend to diffuse through the gold layer, causing tarnishing of its surface and formation of an oxide and/or sulphide layer.

A layer of a suitable barrier metal, usually nickel, is often deposited on the copper substrate before the gold plating. The layer of nickel provides mechanical backing for the gold layer, improving its wear resistance. It also reduces the impact of pores present in the gold layer.

Both the nickel and gold layers can be plated by electrolytic or electroless processes. There are many factors to consider in selection of either electrolytic or electroless plating methods. These include what the deposit will be used for, configuration of the part, materials compatibility and cost of processing. In different applications, electrolytic or electroless plating can have cost advantages.

At higher frequencies, the skin effect may cause higher losses due to higher electrical resistance of nickel; a nickel-plated trace can have its useful length shortened three times in the 1 GHz band in comparison with the non-plated one. Selective plating is used, depositing the nickel and gold layers only on areas where it is required and does not cause the detrimental side effects.[4]

Gold plating may lead to formation of gold whiskers.

Wire bonding between gold plated contacts and aluminium wires or between aluminium contacts and gold wires under certain conditions develops a brittle layer of gold-aluminium intermetallics, known as purple plague.

Soldering issues

Gold-plated printed circuit board

Soldering gold-plated parts can be problematic as gold is soluble in solder. Solder which contains more than 4-5% gold can become brittle. The joint surface is dull-looking.

Gold reacts with both tin and lead in their liquid state, forming brittle intermetallics. When eutectic 63% tin 37% lead solder is used, no lead-gold compounds are formed, because gold preferentially reacts with tin, forming the AuSn
4
compound. Particles of AuSn
4
disperse in the solder matrix, forming preferential cleavage planes, significantly lowering the mechanical strength and therefore reliability of the resulting solder joints.

If the gold layer does not completely dissolve into the solder, then slow intermetallic reactions can proceed in the solid state as the tin and gold atoms cross-migrate. Intermetallics have poor electrical conductivity and low strength. The ongoing intermetallic reactions also cause Kirkendall effect, leading to mechanical failure of the joint, similar to the degradation of gold-aluminium bonds known as purple plague.

A 2-3 µm layer of gold dissolves completely within one second during typical wave soldering conditions. [5] Layers of gold thinner than 0.5 µm (0.02 thou) also dissolve completely into the solder, exposing the underlying metal (usually nickel) to the solder. Impurities in the nickel layer can prevent the solder from bonding to it. Electroless nickel plating contains phosphorus. Nickel with more than 8% phosphorus is not solderable . Electrodeposited nickel may contain nickel hydroxide. An acid bath is required to remove the passivation layer before applying the gold layer; improper cleaning leads to a nickel surface difficult to solder. A stronger flux can help, as it aids dissolving the oxide deposits. Carbon is another nickel contaminant that hinders solderability.

See also

References

  1. Weisberg, Alfred M. (1997). "Gold Plating". Products Finishing Magazine. Retrieved 2013-04-03.
  2. Lechtman, H. (2014). "A Pre-Columbian Technique for Electrochemical Replacement Plating of Gold and Silver on Copper Objects". JOM. 31 (12): 154. doi:10.1007/BF03354479.
  3. G. Horz, M.K. (2000). "The treasure of gold and silver artifacts from the Royal Tombs of Sipan, Peru - a study on the Moche metalworking techniques". Materials Characterization. 45: 391–420. doi:10.1016/s1044-5803(00)00093-0.
  4. "Nickel-gold plating copper PCB traces". Polar Instruments. 2003. Retrieved 2007-03-28.
  5. http://www.tkb-4u.com/articles/soldering/sgons/sgons.php
This article is issued from Wikipedia - version of the 7/7/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.