Collodion process

This deteriorated dry plate portrait of Theodore Roosevelt is similar to a wet plate image but has substantial differences.

The collodion process is an early photographic process.


Description

Collodion process, mostly synonymous with the "collodion wet plate process", requires the photographic material to be coated, sensitized, exposed and developed within the span of about fifteen minutes, necessitating a portable darkroom for use in the field. Collodion is normally used in its wet form, but can also be used in humid ("preserved") or dry form, at the cost of greatly increased exposure time. The latter made the dry form unsuitable for the usual portraiture work of most professional photographers of the 19th century. The use of the dry form was therefore mostly confined to landscape photography and other special applications where minutes-long exposure times were tolerable.

History

The collodion process is said to have been invented in 1851, almost simultaneously, by Frederick Scott Archer and Gustave Le Gray. During the subsequent decades, many photographers and experimenters refined or varied the process. By the end of the 1850s it had almost entirely replaced the first practical photographic process, the daguerreotype.

During the 1880s the collodion process, was largely replaced by gelatin dry platesglass plates with a photographic emulsion of silver halides suspended in gelatin. The dry gelatin emulsion was not only more convenient but could be made much more sensitive, greatly reducing exposure times.

One collodion process, the tintype, was in limited use for casual portraiture by some itinerant and amusement park photographers as late as the 1930s, and the wet plate collodion process was still in use in the printing industry in the 1960s for line and tone work (mostly printed material involving black type against a white background) as for large work it was much cheaper than gelatin film.

21st century

The wet plate collodion process has undergone a revival as an historical technique over the past few decades. There are several practising ambrotypists and tintypists who regularly set up and do images at Civil War re-enactments. Fine art photographers use the process and its handcrafted individuality for gallery showings and personal work. There are several ISTmakers of reproduction equipment exist. The process is taught in workshops around the world and several workbooks and manuals are in print. Many artists work with collodion around the globe, including Kurt Grüng, Sally Mann, and Ben Cauchi.

Advantages

A portable photography studio in 19th century Ireland. The wet collodion process sometimes gave rise to portable darkrooms, as photographic images needed to be developed while the plate was still wet.

The collodion process produced a negative image on a transparent support (glass). This was an improvement over the calotype process, invented by William Henry Fox Talbot, which relied on paper negatives, and the daguerreotype, which produced a one-of-a-kind positive image and could not be replicated. The collodion process, thus combined desirable qualities of the calotype process (enabling the photographer to make a theoretically unlimited number of prints from a single negative) and the daguerreotype (creating a sharpness and clarity that could not be achieved with paper negatives). Collodion printing was typically done on albumen paper.

The collodion process had other advantages, especially in comparison with the daguerreotype. It was a relatively inexpensive process. The polishing equipment and fuming equipment needed for the daguerreotype could be dispensed with entirely. The support for the images was glass, which was far less expensive than silver-plated copper, and was more durable than paper negatives. It was also fast for the time, requiring only seconds for exposure.

Disadvantages

The wet collodion process had a major disadvantage. The entire process, from coating to developing, had to be done before the plate dried. This gave the photographer no more than 10 minutes to complete everything. This made it inconvenient for field use, as it required a portable darkroom. The plate dripped silver nitrate solution, causing stains and troublesome build-ups in the camera and plate holders.

The silver nitrate bath was also a source of problems. It gradually became saturated with alcohol, ether, iodide and bromide salts, dust, and various organic matter. It would lose effectiveness, causing plates to mysteriously fail to produce an image.

As with all preceding photographic processes, the wet-collodion process was sensitive only to blue light. Warm colours appear dark, cool colours uniformly light. A sky with clouds is impossible to render, as the spectrum of white clouds contains about as much blue as the sky. Lemons and tomatoes appear a shiny black, and a blue and white tablecloth appears plain white. Victorian sitters who in collodion photographs look as if they are in mourning might have been wearing bright yellow or pink.[1]

Use

"A Veteran with his Wife", taken by an anonymous photographer, shows a British veteran of the Napoleonic era Peninsular Wars. It is a hand-tinted ambrotype using the set collodion positive process, made circa 1860.

Despite its disadvantages, wet plate collodion became enormously popular. It was used for portraiture, landscape work, architectural photography and art photography. The world's largest wet process collodion glass plate negatives known to survive, measuring 53 inches (1.35 m) x 37 inches (0.94 m), are held at the State Library of New South Wales.[2][3][4]

The wet plate process is used by a number of artists and experimenters, who prefer its aesthetic qualities to those of the more modern gelatin silver process. World Wet Plate Day is staged annually in May for contemporary practitioners.[5]

Search for a dry collodion process

The extreme inconvenience of exposing wet collodion in the field led to many attempts to develop a dry collodion process, which could be exposed and developed some time after coating. A large number of methods were tried, though none was ever found to be truly practical and consistent in operation. Well-known scientists such as Joseph Sidebotham, Richard Kennett, Major Russell and Frederick Charles Luther Wratten attempted, but never met with good results.

Typically, methods involved coating or mixing the collodion with a substance that prevented it from drying quickly. As long as the collodion remained at least partially wet, it retained some of its sensitivity. Common processes involved chemicals such as glycerin, magnesium nitrate, tannic acid and albumen. Others involved more unlikely substances, such as tea, coffee, honey, beer and seemingly unending combinations thereof.

Many methods worked to an extent; they allowed the plate to be exposed hours, or even days, after coating. They all possessed the chief disadvantage, that they rendered the plate extremely slow. An image could require anywhere from three to ten times more exposure on a dry plate than on a wet plate.

Collodion emulsion

In 1864 W. B. Bolton and B. J. Sayce published an idea for a process that would revolutionize photography. They suggested that sensitive silver salts be formed in a liquid collodion, rather than being precipitated, in-situ, on the surface of a plate. A light-sensitive plate could then be prepared by simply flowing this emulsion across the surface of a glass plate; no silver nitrate bath was required.

This idea was soon brought to fruition. First, a printing emulsion was developed using silver chloride. These emulsions were slow, and could not be developed, so they were mostly used for positive printing. Shortly later, silver iodide and silver bromide emulsions were produced. These proved to be significantly faster, and the image could be brought out by development.

The emulsions also had the advantage that they could be washed. In the wet collodion process, silver nitrate reacted with a halide salt; potassium iodide, for example. This resulted in a double replacement reaction. The silver and iodine ions in solution reacted, forming silver iodide on the collodion film. However, at the same time, potassium nitrate also formed, from the potassium ions in the iodide and the nitrate ions in the silver. This salt could not be removed in the wet process. However, with the emulsion process, it could be washed out after creation of the emulsion.

The speed of the emulsion process was unremarkable. It was not as fast as the ordinary wet process, but was not nearly as slow as the dry plate processes. Its chief advantage was that each plate behaved the same way. Inconsistencies in the ordinary process were rare.

Collodion emulsion preparation example

Below is an example of the preparation of a collodion emulsion, from the late 19th century. The language has been adapted to be more modern, and the units of measure have been converted to metric.

4.9 grams of pyroxylin are dissolved in 81.3 ml of alcohol, 148 ml of ether.

13 grams of zinc bromide are dissolved in 29.6 ml of alcohol. Four or five drops of nitric acid are added. This is added to half the collodion made above.

21.4 grams of silver nitrate are dissolved in 7.4 ml of water. 29.6 ml of alcohol are added. This is then poured into the other half of the collodion; the brominized collodion dropped in, slowly, while stirring.

The result is an emulsion of silver bromide. It is left to ripen for 10 to 20 hours, until it attains a creamy consistency. It may then be used or washed, as outlined below.

To wash, the emulsion is poured into a dish and the solvents are evaporated, until the collodion becomes gelatinous. It is then washed with water, followed by a washing in alcohol. After washing, it is re-dissolved in a mixture of ether and alcohol, and is ready for use.

Emulsions created in this manner could be used wet, but they were often coated on the plate and preserved in similar ways to the dry process.

Collodion emulsion plates were developed in an alkaline developer, not unlike those in common use today. An example formula follows.

Part A:

Pyrogallic acid 96 g Alcohol 1 oz.

Part B: Potassium bromide 12 g Distilled Water 30 ml

Part C: Ammonium carbonate 80 g Water 30 ml

When needed for use, mix 0.37 ml of A, 2.72 ml of B and 10.9 ml of C. Flow this over the plate until developed. If a dry plate is used, first wash the preservative off in running water.

See also

References

  1. Art Photography (2010-07-07). "Collodion photography: self-portrait in cyanide". Telegraph.co.uk. Retrieved 2013-03-14.
  2. Davies, Alan (February 2013). "Exhibition guide - The Greatest Wonder of the World" (PDF). State Library of New South Wales. p. 12. Retrieved 23 March 2016.
  3. "Panorama of Sydney and the Harbour, New South Wales, (1875) by Charles Bayliss, Bernard Otto Holtermann :: The Collection :: Art Gallery NSW". www.artgallery.nsw.gov.au. Retrieved 2016-03-23.
  4. "Australia's Holtermann collection of wet plate negatives" (PDF). Journal of Photography of the George Eastman House. 4 (3): 6–8. March 1955. Archived from the original (PDF) on 9 September 2015. Retrieved 23 March 2016.
  5. "Home - World Wet Plate Collodion Day". World Wet Plate Collodion Day. Retrieved 2016-03-23.
Wikimedia Commons has media related to Wet collodion.
This article is issued from Wikipedia - version of the 11/28/2016. The text is available under the Creative Commons Attribution/Share Alike but additional terms may apply for the media files.